Mechanical Properties and Microstructure Evolution of Cold-deformed High-nitrogen Nickel-free Austenitic Stainless Steel during Annealing
The mechanical properties and microstructure evolution of cold-deformed CrMnN austenitic stainless steel annealed in a temperature ranging from 50 ℃ to 650 ℃ for 90 min and at 550 ℃ for different time were investigated by tensile test, micro hardness test, and Transmission Electron Microscope (TEM). The steel was strengthened when it got annealed at temperatures ranging from 100 ℃ to 550 ℃, while it was softened when it got annealed at temperatures ranging from 550 ℃ to 650 ℃. Annealing temperature had stronger effect on mechanical properties than annealing time. TEM observations showed that nano-sized precipitates formed when the steel was annealed at 150 ℃ for 90 min, but the size and density of precipitates had no noticeable change with annealing temperature and time. Recrystallization occurred when the steel was annealed at temperatures above 550 ℃ for 90 min, and its scale increased with annealing temperature. Nano-sized annealing twins were observed. The mechanisms that controlled the mechanical behaviors of the steel were discussed.徐明舟,刘春明 - 武汉理工大学学报(材料科学版)(英文版)文章来源： 万方数据 -
Ф10mm碳纤维复合材料管成型工艺及性能研究
对外径为Ф10mm碳纤维复合材料管成型工艺及性能进行了研究.结果表明,采用热缩工艺成型的碳纤维复合材料管工艺简单、质量可靠,Ф10mm碳纤维复合材料管件弯曲刚度与不锈钢管相当,弯曲强度为不锈钢的3倍以上,质量仅为不锈钢的50%,尺寸精度满足设计要求.赵锐霞,尹亮,潘玲英,董波 - 宇航材料工艺文章来源： 万方数据 -
纳米碳化硅改性聚四氟乙烯复合材料的摩擦磨损性能
采用不同偶联剂对纳米碳化硅进行表面处理后,制备了聚四氟乙烯/纳米碳化硅复合材料,考察了偶联剂种类和含量随载荷变化对复合材料摩擦磨损性能的影响,并利用扫描电子显微镜观察和分析了复合材料磨损表面形貌及其磨损机理.结果表明,经表面处理的纳米碳化硅填充后的复合材料硬度和摩擦磨损性能均有提高,以钛酸酯偶联剂(NDZ101)处理效果最好;随着偶联剂含量的增大,钛酸酯偶联剂(NDZ101)处理的复合材料的磨损量和摩擦因数均增大,偶联剂最佳含量为填料质量的1%;偶联剂处理后的纳米碳化硅与基体之间形成了良好的界面,复合材料的磨损以黏着磨损和磨粒磨损为主.路琴,吕少卉,何春霞 - 中国塑料文章来源： 万方数据